Polycarbonate Films Spec. | ||||
Property | Test Method | Units | Value | |
Physical | ||||
Specific Gravity | ASTM D792 | G/cm3 | 1.2 | |
Water Absorption Equilibrium,24Hrs | ASTM D570 | % | 0.35 | |
Tensile Strength | ASTM D882 | Psi | 8,800 | |
ISO R1184-1987 | Mpa | 60 | ||
Elongation Ultimate | ASTM D882 | % | >90 | |
Impact Strength @ 10mils | JIS-k6745 | In-ibs | 120 | |
Tear Strength Propagation | ASTM D1922 | G/mil | >30 | |
Temperature Resistance | ||||
Vicat Softening Temperature | ASTM D1525 | ℃ | 110 | |
Heat Shrinkage Rate | ASTM D1204 | % | <1.0 | |
Electrical | ||||
Dielectric Strength (@ 10 mils) | ASTM D149 | V/mil | 1700 | |
Volume Resistivity @25℃,50%RH | ASTM D257 | Ohm.m | 1016 | |
Surface Resistivity @25℃,50%RH | ASTM D257 | Ohm | 1015 | |
Flammability | ||||
UL Flammability | UL BULLETIN94 | |||
@ ≥ 10 mils | UL94 | V0 | ||
@ ＜ 10 mils | UL94 | VTM-0 | ||
Property | Unit | Ultimate Value | ||
Gaute Variation | % | ＞0.5 ±0.006mm | ||
≦0.5 ±0.004mm | ||||